3 - Layer SYSTEMS PERFORMANCES

LAYER	MATERIAL	AVERAGE THICKNESS
1^ST	EPOXY RESIN	80 - 200 µm
2^ND	ADHESIVE	250 µm
3^RD	TOP COAT	2,5 µm

	P.CO.LD


	1^st Layer EPOXY PRIMER 2^nd Layer COESIVE^® L.8.92.8 (m) 3^rd Layer LUXENE^® LDPE AM/97	Max Service Temperature: 60°C Standard Reference: DIN 30670 NF A 49-710

PROPERTY	CONDITION	UNIT	DIN 30670	NF A 49-710	VALUE
Peeling test	T=23°C T=50°C T=70°C	N/cm	≥35 ≥25	≥80 ≥20	≥300 ≥150 ≥70
Identation Resistance	T=23°C T=50°C	mm	≤0.2 ≤0.3	≤0.3	≤0.2 ≤0.3
Elongation at break		%	≥200	≥300	≥300
Impact Resistance	T=23°C	J/mm	≥5	≥5	≥5
Coating Resistivity	100 DAYS	Ωm²	≥108	≥108	≥109

Note: The data reported cannot be considered as specification limits

	P.CO.HD


	1^st Layer EPOXY PRIMER 2^nd Layer COESIVE^® L.8.92.8 (m) 3^rd Layer LUXENE^® HDPE 2050	Max Service Temperature: 85°C Standard Reference: DIN 30670 NF A 49-710

PROPERTY	CONDITION	UNIT	DIN 30670	NF A 49-710	VALUE
Peeling test	T=23°C T=50°C T=70°C	N/cm	≥35 ≥25	≥80 ≥20	≥300 ≥150 ≥70
Identation Resistance	T=23°C T=50°C T=70°C	mm	≤0.2 ≤0.3 ≤0.3	≤0.3 ≤1.0	≤0.2 ≤0.3 ≤0.3
Elongation at break		%	≥200	≥300	≥300
Impact Resistance	T=23°C	J/mm	≥5	≥5	≥5
Coating Resistivity	100 DAYS	Ωm²	≥10⁸	≥10⁸	≥10⁹

Note: The data reported cannot be considered as specification limits

	PP.N


	1^st Layer EPOXY PRIMER 2^nd Layer PROESIVE RG.10^® 3^rd Layer PROCOAT^® H.08HT	Max Service Temperature: 110°C Standard Reference: DIN 30678 NF A 49-711

PROPERTY	CONDITION	UNIT	DIN 30670	NF A 49-711	VALUE
Peeling test	T=23°C T=50°C T=90°C T=110°C	N/cm	≥100 ≥80	≥150 ≥40	≥300 ≥200 ≥150 ≥80
Identation Resistance	T=23°C T=90°C T=110°C	mm	≤0.3	≤0.1 ≤0.4	≤0.1 ≤0.3 ≤0.4
Elongation at break		%	≥300	≥400	≥400
Impact Resistance	T=0°C T=23°C	J/mm	≥5	≥10	≥5 ≥10
Coating Resistivity	100 DAYS	Ωm²	≥108	≥108	≥109

Note: The data reported cannot be considered as specification limits

	PP.H


	1^st Layer EPOXY PRIMER 2^nd Layer PROESIVE^® H.03.HT 3^rd Layer PROCOAT^® H.08.HT	Max Service Temperature: 140°C

PROPERTY	CONDITION	UNIT	VALUE
Peeling test	T=23°C T=140°C	N/cm	≥300 ≥80
Identation Resistance	T=23°C T=90°C T=110°C	mm	≤0.1 ≤0.3 ≤0.4
Elongation at break		%	≥400
Impact Resistance	T=23°C	J/mm	≥10
Coating Resistivity	100 DAYS	Ωm²	≥10⁹

Note: The data reported cannot be considered as specification limits